 产品详细介绍 |
|
项 目 \ 牌 号 |
CN-42 |
CN-40 |
CL-80 |
PZCL-78 |
CL-75 |
CL-65 |
CL-55 |
CL-80E |
CL-70E |
HA-60E |
HA-75E |
UH85K |
MA-A89 |
WMA-A92 |
| Al2O3 % |
≥42 |
≥40
|
≥80.0
|
≥78.0
|
≥75.0
|
≥65.0
|
≥55.0
|
≥80
|
≥70
|
≥60
|
≥75
|
≥85
|
≥86
|
≥92
|
| Fe2O3 % |
|
|
≤2.0 |
≤2.0
|
|
|
|
≤1.5
|
≤1.6
|
≤1.5 |
≤1.5 |
≤2.0
|
≤0.5 |
≤0.5
|
| TiO2 % |
|
|
|
|
|
|
|
|
≤3.5 |
|
|
|
|
≤0.1
|
| MgO % |
|
|
|
|
|
|
|
|
|
|
|
|
≥4.5
|
4-8
|
| SiO2 % |
|
|
|
|
|
|
|
|
|
|
|
|
≤2.5 |
≤0.5 |
| 耐火度 ℃ |
≥1760
|
≥1740
|
|
|
|
|
|
|
|
≥1850
|
≥1850
|
|
|
|
| 荷重软化温度KD ℃ |
≥1430 |
≥1400 |
≥1530 |
≥1550 |
≥1510 |
≥1490 |
≥1470 |
T2≥1550 |
T2≥1520 |
T2≥1600 |
T2≥1650 |
T2≥1500 |
T2≥1650 |
T0.5≥1550 |
| 高温抗折1500 ℃ MPa |
|
|
|
|
|
|
|
|
|
|
|
|
|
≥2.0 |
| 重烧线变化率 % |
1400℃×2h
0～-0.3 |
1400℃×2h
0～-0.3
|
1550℃×2h
0.1～-0.5 |
1550℃×2h
0.4～-0.3 |
1500℃×2h
0.1～-0.5 |
1500℃×2h
0.1～-0.5 |
1450℃×2h
0.1～-0.5 |
1500℃×2h
-0.1～+0.5 |
1500℃×2h
-0.1～+0.5 |
1500℃×2h
0～+1.0 |
1500℃×2h
0～+1.0 |
1500℃×5h
>+0.5 |
1600℃×3h
0～+0.5 |
1500℃×5h
-0.3～+0.3 |
| 显气孔率 % |
≤18 |
≤19 |
≤24 |
≤21 |
≤28 |
≤28 |
≤22 |
≤19
|
≤20
|
≤17
|
≤19
|
≤19
|
≤19
|
≤22
|
| 体积密度 g/cm3 |
|
|
|
|
|
|
|
≥2.75
|
≥2.5
|
≥2.60
|
≥2.65
|
≥2.80
|
≥3.0
|
≥3.05
|
| 常温耐压强度 Mpa |
≥39.2 |
≥34.3 |
≥50 |
≥70 |
≥40 |
≥35 |
≥45 |
≥60 |
≥60 |
≥60 |
≥60 |
≥50 |
≥60 |
≥40 | | | |
|