Item项 目 / Brand牌 号 |
Al2O3-SiC-C质高炉出铁沟浇注料 Al2O3-SiC-C castable for blast furnace tapping channel
|
钢包用铝尖晶石耐火浇注料 alumina-spinel castable for ladle |
高铝可塑料 high-alumina plastic castable
|
TG-11 |
TG-12 |
TG-13 |
TG-14 |
|
AM-85 |
|
JS-1600 |
Al2O3 %
|
≥60
|
≥50
|
≥45
|
≥45
|
≥70
|
≥85
|
≥55
|
≥65
|
SiC+C %
|
≥12
|
≥30
|
≥7
|
≥12
|
MgO≥12 |
MgO≥10 |
SiO2≤40 |
SiO2≤30 |
CaO % |
≤1.5
|
≤1.5
|
≤1.5
|
≤1.5
|
|
|
|
|
Bulk Density体积密度 g/cm3
|
110℃×24h
|
≥2.7 |
≥2.6 |
≥2.4 |
≥2.4 |
≥2.8
|
≥3.0
|
≥2.3
|
≥2.4
|
1000℃×3h
|
|
|
|
|
≥2.7
|
≥2.9
|
|
|
1450℃×3h
|
≥2.6
|
≥2.5
|
≥2.35
|
≥2.35
|
1500℃×3h ≥2.9
|
1500℃×3h≥3.1
|
|
|
Cold Crushing Strength耐压强度 MPa
|
110℃×24h
|
≥30
|
≥20
|
≥30
|
≥20
|
≥40
|
≥40
|
|
|
1450℃×3h
|
≥40
|
≥30
|
≥40
|
≥30
|
≥60
|
≥60
|
|
|
Modulus of Rupture抗折强度 MPa
|
110℃×24h
|
≥5 |
≥4
|
≥5
|
≥4
|
≥5
|
≥6
|
5~7
|
5~8
|
1000℃×3h
|
|
|
|
|
≥8
|
≥8
|
|
|
1450℃×3h
|
≥5
|
≥5
|
≥6
|
≥5
|
1500℃×3h ≥10
|
1500℃×3h ≥12
|
1500℃×3h ≥10
|
1500℃×3h ≥12
|
Linear Change After Heating烧后线变化率 % |
110℃×24h
|
|
|
|
|
0~-0.1
|
0~-0.1
|
-0.2~0 |
-0.2~0 |
1000℃×3h |
|
|
|
|
0~+0.2 |
0~+0.2 |
|
|
1450℃×3h |
±0.5 |
±0.5 |
±0.6 |
±0.6 |
1500℃×3h 0~+0.8 |
1500℃×3h 0~+0.8 |
1500℃×3h 0~+0.5 |
1500℃×3h 0~+0.5 |
Max service temperature最高使用温度 /℃ |
|
|
|
|
1760 |
1800 |
1500 |
1600 |
使用部位Using area |
主沟 铁水线 |
主沟 渣线 |
铁水沟 |
用于 渣沟 |
用于钢包内衬,振动浇铸法施工 |
用于轧钢加热炉、各种焚烧炉 和其它工业窑炉内衬,捣固法施工 |